eSun Filament PLA-Silk Mystic 1.75mm (blue-orange-green) (PLA-SKMC175S-UOG1P1)

eSun PLA-Silk Mystic 1.75 mm Filament
eSun PLA-Silk Mystic 1.75 mm filament is a 3D printing material made from modified PLA, characterized by a silky sheen and a three-color effect. The blue-orange-green color scheme makes the printed models change their appearance depending on the viewing angle. The material combines an attractive finish with the ease of printing characteristic of PLA. It is suitable for creating figurines, decorations, ornaments, and other models where surface appearance is important. The spool contains 1 kg of filament.


Three colors and a silky sheen
Thanks to the combination of multiple colors in a single filament, the finished prints take on a unique appearance. As you rotate the model, different color combinations become visible, changing depending on the viewing angle. The silky sheen gives the surface a smooth, decorative appearance, making figurines, vases, and ornaments look attractive without the need for painting. This solution is particularly useful for projects where the visual effect is key.


Easy printing and good material properties
PLA-Silk Mystic filament produces aesthetically pleasing prints when the printer settings are properly adjusted. The recommended nozzle temperature is 190–230°C, and the recommended heated bed temperature is 45–60°C. A heated bed is required. The material allows printing at speeds of up to 200 mm/s; however, to achieve a more pronounced gloss, it is advisable to slow down the printing of outer walls. The tensile strength in the XY plane is 40.13 MPa, and the flexural strength in the same plane is 60.2 MPa. The heat deflection temperature is 54.7°C, so this filament is best suited for decorative models and lightly loaded parts that will not be exposed to high temperatures.




 



Manufacturer eSUN
Model PLA-SKMC175S-UOG1P1
Filament Type PLA-Silk Mystic
Material modified PLA
Color blue-orange-green
Filament Diameter 1.75 mm
Filament Weight 1 kg
Density 1.23 g/cm³
Melt Flow Index (MFI) 4.5 g/10 min (190°C / 2.16 kg)
Nozzle Temperature 190–230°C
Bed temperature 45–60°C
Heated bed required
Print speed up to 200 mm/s
Fan speed 100%
Heat Deflection Temperature (HDT) 54.7°C
Tensile strength (XY / Z) 40.13 / 12.88 MPa
Elongation at break (XY / Z) 5.39 / 1.3%
Flexural strength (XY / Z) 60.2 / 19.2 MPa
Flexural modulus (XY / Z) 2849.66 / 2579.63 MPa
Izod impact strength (XY / Z) 3.01 / 1.9 kJ/m²